IRIS è la soluzione IT che facilita la raccolta e la gestione dei dati relativi alle attività e ai prodotti della ricerca. Fornisce a ricercatori, amministratori e valutatori gli strumenti per monitorare i risultati della ricerca, aumentarne la visibilità e allocare in modo efficace le risorse disponibili.
EnglishA high-purity MgB4 phase has been synthesized and used as the precursor powder for the realization of in situ wires. Various final heat treatments, from 550 to 1100 ◦C for 20 min each, have been carried out to convert the inner mixture to MgB2 . Critical current densities up to 1.75 × 106 and 0.98 × 106 A cm−2 at 4.2 and 20 K, with 0.2 T, up to 0.76 × 105 A cm−2 at 4.2 K and 4 T, and up to 0.78 × 105 A cm−2 at 20 K and 2 T were measured. Critical temperatures up to 38.5 K were measured. These results suggest that this could be a good alternative to both ex situ and classical in situ routes.
Scheda prodotto non validato
Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo
| Titolo: | Large critical current density in MgB2wire using MgB4as precursor | |
| Autori: | ||
| Data di pubblicazione: | 2013 | |
| Rivista: | ||
| Abstract: | A high-purity MgB4 phase has been synthesized and used as the precursor powder for the realization of in situ wires. Various final heat treatments, from 550 to 1100 ◦C for 20 min each, have been carried out to convert the inner mixture to MgB2 . Critical current densities up to 1.75 × 106 and 0.98 × 106 A cm−2 at 4.2 and 20 K, with 0.2 T, up to 0.76 × 105 A cm−2 at 4.2 K and 4 T, and up to 0.78 × 105 A cm−2 at 20 K and 2 T were measured. Critical temperatures up to 38.5 K were measured. These results suggest that this could be a good alternative to both ex situ and classical in situ routes. | |