Pure ZrB2 and ZrB2-SiC composites were joined to Ti6Al4V at 1100°C using B-Ni50 (at.%) as a filler alloy. The brazing medium and the processing parameters were chosen on the basis of specific wetting tests which showed the good adhesion properties of the B-Ni alloy with both the ceramic and the Ti alloy; interfacial reactions were foreseen and interpreted by phase diagram analysis.A multilayer metal-ceramic interfacial structure was observed in the joints and a key role was played by Ti coming from Ti6Al4V: it worked as the active element enhancing the adhesion of the liquid on to the ceramic and segregated at the interface forming TiB. A satisfactory mechanical performance was obtained for ZrB2-SiC/Ti6Al4V joints, which exhibited a room temperature shear strength of 74 MPa.

Joining of ZrB2 ceramics to Ti6Al4V by Ni-based interlayers

ARTINI, CRISTINA;CIRILLO, PAOLO;
2014-01-01

Abstract

Pure ZrB2 and ZrB2-SiC composites were joined to Ti6Al4V at 1100°C using B-Ni50 (at.%) as a filler alloy. The brazing medium and the processing parameters were chosen on the basis of specific wetting tests which showed the good adhesion properties of the B-Ni alloy with both the ceramic and the Ti alloy; interfacial reactions were foreseen and interpreted by phase diagram analysis.A multilayer metal-ceramic interfacial structure was observed in the joints and a key role was played by Ti coming from Ti6Al4V: it worked as the active element enhancing the adhesion of the liquid on to the ceramic and segregated at the interface forming TiB. A satisfactory mechanical performance was obtained for ZrB2-SiC/Ti6Al4V joints, which exhibited a room temperature shear strength of 74 MPa.
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11567/718000
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 25
  • ???jsp.display-item.citation.isi??? 22
social impact