On the melt processed YBa2Cu3O7−x physico-chemical characterization

Costa, G.A.; Ferretti, M.; Olcese, G.L.; Calzona, V.; Cimberle, M.R.; Ferdeghini, C.; Putti, M.; Siri, A.S.

doi:10.1016/0038-1098(88)90135-4

CINECA IRIS Institutional Research Information System

IRIS è la soluzione IT che facilita la raccolta e la gestione dei dati relativi alle attività e ai prodotti della ricerca. Fornisce a ricercatori, amministratori e valutatori gli strumenti per monitorare i risultati della ricerca, aumentarne la visibilità e allocare in modo efficace le risorse disponibili.

We determined the proper conditions to obtain superconducting samples by melting. Two preparation methods were investigated: arc melting of YBa2Cu3O7 prereacted powders at about 1900°C and partial melting at T = 1080°C, just 50°C above the peritectic decomposition of YBa2Cu3O7. The latter one revealed itself a one-step technique to obtain high Tc superconductors by melting. Micrographic, structural, electric and magnetic characterizations of these materials are reported and compared with the corresponding properties of the more traditional sintered samples: the best results were obtained for the partially melted samples annealed in flowing oxygen at suitable temperature.

Scheda prodotto non validato

Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo

SFX

Utilizza questo identificativo per citare o creare un link a questo documento: http://hdl.handle.net/11567/378831

Titolo:	On the melt processed YBa2Cu3O7−x physico-chemical characterization
Autori interni:	COSTA, GIORGIO FERRETTI, MAURIZIO PUTTI, MARINA SIRI, ANTONIO
Data di pubblicazione:	1988
Rivista:	SOLID STATE COMMUNICATIONS
Abstract:	We determined the proper conditions to obtain superconducting samples by melting. Two preparation methods were investigated: arc melting of YBa2Cu3O7 prereacted powders at about 1900°C and partial melting at T = 1080°C, just 50°C above the peritectic decomposition of YBa2Cu3O7. The latter one revealed itself a one-step technique to obtain high Tc superconductors by melting. Micrographic, structural, electric and magnetic characterizations of these materials are reported and compared with the corresponding properties of the more traditional sintered samples: the best results were obtained for the partially melted samples annealed in flowing oxygen at suitable temperature.
Handle:	http://hdl.handle.net/11567/378831
Appare nelle tipologie:	01.01 - Articolo su rivista