IRIS è la soluzione IT che facilita la raccolta e la gestione dei dati relativi alle attività e ai prodotti della ricerca. Fornisce a ricercatori, amministratori e valutatori gli strumenti per monitorare i risultati della ricerca, aumentarne la visibilità e allocare in modo efficace le risorse disponibili.
EnglishThe YbAu2-xSix and CaAu2-xSix systems were studied by X-ray techniques in the range 0.7 ≤ x ≤ 1.3. The YbAuSi compound forms peritectically at 1478 K and is stable till 1168 K in its high-temperature form (EuAuGe type); below 1168 K the SrAgGe type occurs. No equiatomic compound exists in the Ca-Au-Si system. In the gold- and silicon-rich regions the two systems show similar structural behaviour: the gold-rich phases belong to the CeCu2 or the EuAuGe type, while the silicon-rich phases crystallize in the AlB2 type. The magnetic susceptibility at room temperature indicates the divalency of ytterbium in YbAuSi.
Scheda prodotto non validato
Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo
http://hdl.handle.net/11567/333202| Titolo: | New phases in the Yb-Au-Si and Ca-Au-Si systems |
| Autori interni: | PANI, MARCELLA MERLO, FRANCO FORNASINI, MARIA LUISA |
| Data di pubblicazione: | 1999 |
| Rivista: | ZEITSCHRIFT FUR KRISTALLOGRAPHIE |
| Abstract: | The YbAu2-xSix and CaAu2-xSix systems were studied by X-ray techniques in the range 0.7 ≤ x ≤ 1.3. The YbAuSi compound forms peritectically at 1478 K and is stable till 1168 K in its high-temperature form (EuAuGe type); below 1168 K the SrAgGe type occurs. No equiatomic compound exists in the Ca-Au-Si system. In the gold- and silicon-rich regions the two systems show similar structural behaviour: the gold-rich phases belong to the CeCu2 or the EuAuGe type, while the silicon-rich phases crystallize in the AlB2 type. The magnetic susceptibility at room temperature indicates the divalency of ytterbium in YbAuSi. |