In the present work a macroporous brushite bone cement for use either as an injected or mouldable paste, or in the shape of preformed grafts, has been investigated. Macropores have been introduced by adding to the powder single crystals of mannitol which worked as a porogen. The size of the crystals was in the range of 250–500 lm in diameter, suitable for cell infiltration, with a shape ratio between 3 and 6. From compression tests on cylindrical samples an elastic modulus in the range 2.5–4.2 GPa and a compressive strength in the range 17.5–32.6 MPa were obtained for a volume fraction of macropores varying between 15 and 0%. Thus the compressive strength exceeded in all tests the maximum value currently attributed to cancellous bone.

Preparation and properties of macroporous brushite bone cements

BARBERIS, FABRIZIO;BOTTER, RODOLFO;CAPURRO, PIETRO MARCO;QUARTO, RODOLFO;FINOCCHIO, ELISABETTA;MUSSI, VALENTINA;VALBUSA, UGO
2009-01-01

Abstract

In the present work a macroporous brushite bone cement for use either as an injected or mouldable paste, or in the shape of preformed grafts, has been investigated. Macropores have been introduced by adding to the powder single crystals of mannitol which worked as a porogen. The size of the crystals was in the range of 250–500 lm in diameter, suitable for cell infiltration, with a shape ratio between 3 and 6. From compression tests on cylindrical samples an elastic modulus in the range 2.5–4.2 GPa and a compressive strength in the range 17.5–32.6 MPa were obtained for a volume fraction of macropores varying between 15 and 0%. Thus the compressive strength exceeded in all tests the maximum value currently attributed to cancellous bone.
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11567/246282
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 43
  • ???jsp.display-item.citation.isi??? 35
social impact