This paper deals with characterizing the bridging mechanisms developed across delamination cracks by through-thickness reinforcement, using stitched carbon/epoxy laminates under mode II loading as a prime example. End Notched Flexure (ENF) tests are performed which show that stitching can provide stable crack growth. The bridging law, which characterizes the bridging action of the stitches, is deduced from both crack profile measurements and load vs. deflection curves. Consistent results are obtained from the two methods. The inferred laws imply that delamination cracks will commonly grow in conditions that are neither accurately nor properly described by linear elastic fracture mechanics. Large scale bridging calculations are required, in which the essential material property is the bridging traction law. The level of detail in which the law must be determined can be inferred from the sensitivity of predicted crack growth to variations in the law. It is recommended that the required parametric traction law be deduced in engineering practice from load vs, deflection data from the standard ENF (or similar) test, with due regard to selecting the notch size and other specimen dimensions to ensure that crack growth is stable in the test.

Characterizing mode II delamination cracks in stitched composites

MASSABO', ROBERTA;
1998-01-01

Abstract

This paper deals with characterizing the bridging mechanisms developed across delamination cracks by through-thickness reinforcement, using stitched carbon/epoxy laminates under mode II loading as a prime example. End Notched Flexure (ENF) tests are performed which show that stitching can provide stable crack growth. The bridging law, which characterizes the bridging action of the stitches, is deduced from both crack profile measurements and load vs. deflection curves. Consistent results are obtained from the two methods. The inferred laws imply that delamination cracks will commonly grow in conditions that are neither accurately nor properly described by linear elastic fracture mechanics. Large scale bridging calculations are required, in which the essential material property is the bridging traction law. The level of detail in which the law must be determined can be inferred from the sensitivity of predicted crack growth to variations in the law. It is recommended that the required parametric traction law be deduced in engineering practice from load vs, deflection data from the standard ENF (or similar) test, with due regard to selecting the notch size and other specimen dimensions to ensure that crack growth is stable in the test.
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11567/190186
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 58
  • ???jsp.display-item.citation.isi??? 45
social impact