We report results of steady-state photoinduced absorption experiments on PDA-4BCMU grown and oriented on silica substrate. A high degree of axial order, checked by linear and nonlinear optical dichroism and correlated with X-ray measurements was found. Polycrystalime films were obtained with a preferential orientation of crystallites. Unlike the solution cast films exhibiting the so called ,,red form" only, the deposited films are blue thus showing a better it-electron conjugation than in the former case due to a better planarity of polymer chains. The films were used to perform steady-state photoinduced absorption experiments. Three photomduced absorption bands at 0.82, 0.95, and 1.39 eV were observed. The 0.82 and 0.95 eV absorption features are assigned to charged states while the 1.39 eV peak is originated by triplet excitons. The photogeneration in PDA-4BCMU of both charged and neutral states is discussed and compared with the results obtained in polydiacetylenes having carbazolyl groups as substituents. The relative weight of one excited species over the other one is dictated by the molecular and supramolecular organization ofthe polymer

On the nature of long-lived photoexcited states in polydiacetylenes: The photoinduced absorption spectra of PDA-4BCMU

COMORETTO, DAVIDE;ALLOISIO, MARINA;MUSSO, GIANFRANCO;OTTONELLI, MASSIMO;DELLEPIANE, GIOVANNA;
1999

Abstract

We report results of steady-state photoinduced absorption experiments on PDA-4BCMU grown and oriented on silica substrate. A high degree of axial order, checked by linear and nonlinear optical dichroism and correlated with X-ray measurements was found. Polycrystalime films were obtained with a preferential orientation of crystallites. Unlike the solution cast films exhibiting the so called ,,red form" only, the deposited films are blue thus showing a better it-electron conjugation than in the former case due to a better planarity of polymer chains. The films were used to perform steady-state photoinduced absorption experiments. Three photomduced absorption bands at 0.82, 0.95, and 1.39 eV were observed. The 0.82 and 0.95 eV absorption features are assigned to charged states while the 1.39 eV peak is originated by triplet excitons. The photogeneration in PDA-4BCMU of both charged and neutral states is discussed and compared with the results obtained in polydiacetylenes having carbazolyl groups as substituents. The relative weight of one excited species over the other one is dictated by the molecular and supramolecular organization ofthe polymer
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: http://hdl.handle.net/11567/608141
 Attenzione

Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo

Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 61
  • ???jsp.display-item.citation.isi??? ND
social impact