The low temperature heat capacity and magnetization were measured for the Pr,Co,Al, intermetallic compound. A ferromagnetic transition was observed at 4.5 K with a saturation value of the magnetic moment of the Pr atom in the ordered state of 1.1 mu(B) at 2.5 K. In the paramagnetic region the compound follows the Curie-Weiss law with mu(eff) = 3.59 mu(B) and theta(P) = +5 K. Above the magnetic transition an estimate of the electronic coefficient of the specific heat was obtained.
Thermodynamic, electric and magnetic properties of Pr7Co6Al7 intermetallic compound
CANEPA, FABIO MICHELE;MANFRINETTI, PIETRO;CIRAFICI, SALVINO;
1999-01-01
Abstract
The low temperature heat capacity and magnetization were measured for the Pr,Co,Al, intermetallic compound. A ferromagnetic transition was observed at 4.5 K with a saturation value of the magnetic moment of the Pr atom in the ordered state of 1.1 mu(B) at 2.5 K. In the paramagnetic region the compound follows the Curie-Weiss law with mu(eff) = 3.59 mu(B) and theta(P) = +5 K. Above the magnetic transition an estimate of the electronic coefficient of the specific heat was obtained.File in questo prodotto:
Non ci sono file associati a questo prodotto.
I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.