Excitons dominate the light absorption and re-emission spectra of monolayer transition-metal dichalcogenides (TMD). Microscopic investigations of the excitonic response in TMD almost invariably extract information from the radiative recombination step, which only constitutes one part of the picture. Here, by exploiting imaging spectroscopic ellipsometry (ISE), we investigate the spatial dependence of the dielectric function of chemical vapor deposition (CVD)-grown WS2 flakes with a microscopic lateral resolution, thus providing information about the spatially varying, exciton-induced light absorption in the monolayer WS2. Comparing the ISE results with imaging photoluminescence spectroscopy data, the presence of several correlated features was observed, along with the unexpected existence of a few uncorrelated characteristics. The latter demonstrates that the exciton-induced absorption and emission features are not always proportional at the microscopic scale. Microstructural modulations across the flakes, having a different influence on the absorption and re-emission of light, are deemed responsible for the effect.

Local Optical Properties in CVD-Grown Monolayer WS2Flakes

Magnozzi M.;Ferrera M.;Canepa P.;Cavalleri O.;Coletti C.;Bisio F.;Canepa M.
2021-01-01

Abstract

Excitons dominate the light absorption and re-emission spectra of monolayer transition-metal dichalcogenides (TMD). Microscopic investigations of the excitonic response in TMD almost invariably extract information from the radiative recombination step, which only constitutes one part of the picture. Here, by exploiting imaging spectroscopic ellipsometry (ISE), we investigate the spatial dependence of the dielectric function of chemical vapor deposition (CVD)-grown WS2 flakes with a microscopic lateral resolution, thus providing information about the spatially varying, exciton-induced light absorption in the monolayer WS2. Comparing the ISE results with imaging photoluminescence spectroscopy data, the presence of several correlated features was observed, along with the unexpected existence of a few uncorrelated characteristics. The latter demonstrates that the exciton-induced absorption and emission features are not always proportional at the microscopic scale. Microstructural modulations across the flakes, having a different influence on the absorption and re-emission of light, are deemed responsible for the effect.
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11567/1065022
 Attenzione

Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo

Citazioni
  • ???jsp.display-item.citation.pmc??? 1
  • Scopus 10
  • ???jsp.display-item.citation.isi??? 9
social impact