We report on the growth of epitaxial Fe1+δSe0.5Te0.5thin films on 0°, 5°, 10°, 15° and 20° vicinal cut CaF2single crystals by pulsed laser deposition. In situ electron and ex situ x-ray diffraction studies reveal a tilted growth of the Fe1+δSe0.5Te0.5films, whereby under optimized deposition conditions the c-axis alignment coincides with the substrate [001] tilted axis up to a vicinal angle of 10°. Atomic force microscopy shows a flat island growth for all films. From resistivity measurements in longitudinal and transversal directions, the ab- and c-axis components of resistivity are derived and the mass anisotropy parameter is determined. Analysis of the critical current density indicates that no effective c-axis correlated defects are generated by vicinal growth, and pinning by normal point core defects dominates. However, for H||ab the effective pinning centers change from surface defects to point core defects near the superconducting transition due to the vicinal cut. Furthermore, we show in angular-dependent critical current density data a shift of the ab-planes maxima position with the magnetic field strength.

Deposition and properties of Fe(Se,Te) thin films on vicinal CaF2substrates

Putti, Marina;
2017-01-01

Abstract

We report on the growth of epitaxial Fe1+δSe0.5Te0.5thin films on 0°, 5°, 10°, 15° and 20° vicinal cut CaF2single crystals by pulsed laser deposition. In situ electron and ex situ x-ray diffraction studies reveal a tilted growth of the Fe1+δSe0.5Te0.5films, whereby under optimized deposition conditions the c-axis alignment coincides with the substrate [001] tilted axis up to a vicinal angle of 10°. Atomic force microscopy shows a flat island growth for all films. From resistivity measurements in longitudinal and transversal directions, the ab- and c-axis components of resistivity are derived and the mass anisotropy parameter is determined. Analysis of the critical current density indicates that no effective c-axis correlated defects are generated by vicinal growth, and pinning by normal point core defects dominates. However, for H||ab the effective pinning centers change from surface defects to point core defects near the superconducting transition due to the vicinal cut. Furthermore, we show in angular-dependent critical current density data a shift of the ab-planes maxima position with the magnetic field strength.
File in questo prodotto:
File Dimensione Formato  
Bryja_2017_Supercond._Sci._Technol._30_115008.pdf

accesso chiuso

Tipologia: Documento in versione editoriale
Dimensione 2.31 MB
Formato Adobe PDF
2.31 MB Adobe PDF   Visualizza/Apri   Richiedi una copia

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11567/939854
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 8
  • ???jsp.display-item.citation.isi??? 8
social impact