Understanding the effects of impurities, segregation, undercooling, and solidification velocity is necessary to reconstruct prehistoric As-Cu alloy manufacturing processes and practices. Moreover, these alloys often contain a wide variety of minor and trace elements such that the binary As-Cu equilibrium phase diagram does not adequately represent arsenical bronze artifacts as-cast in ancient molds. Furthermore, the variable cooling rates present in as-cast alloys of predominantly arsenic and copper, due to the thermal properties of differing mold materials, would have had profound effects on the formation of inversely segregated arsenic. Alloys with 1 to 15 wt pct arsenic were prepared and studied using differential thermal analysis, metallography, and scanning electron microscopy with energy-dispersive X-ray spectroscopy. Equilibrium diagrams were established and the potential influence of trace elements discussed. A new liquidus curve for the equilibrium diagram in this compositional range, measuring slightly higher in temperature, was established.

Archaeological Arsenical Bronzes and Equilibrium in the As-Cu System

DANIELE MACCIO´;
2018-01-01

Abstract

Understanding the effects of impurities, segregation, undercooling, and solidification velocity is necessary to reconstruct prehistoric As-Cu alloy manufacturing processes and practices. Moreover, these alloys often contain a wide variety of minor and trace elements such that the binary As-Cu equilibrium phase diagram does not adequately represent arsenical bronze artifacts as-cast in ancient molds. Furthermore, the variable cooling rates present in as-cast alloys of predominantly arsenic and copper, due to the thermal properties of differing mold materials, would have had profound effects on the formation of inversely segregated arsenic. Alloys with 1 to 15 wt pct arsenic were prepared and studied using differential thermal analysis, metallography, and scanning electron microscopy with energy-dispersive X-ray spectroscopy. Equilibrium diagrams were established and the potential influence of trace elements discussed. A new liquidus curve for the equilibrium diagram in this compositional range, measuring slightly higher in temperature, was established.
File in questo prodotto:
Non ci sono file associati a questo prodotto.

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11567/928876
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 6
  • ???jsp.display-item.citation.isi??? 5
social impact