IRIS è la soluzione IT che facilita la raccolta e la gestione dei dati relativi alle attività e ai prodotti della ricerca. Fornisce a ricercatori, amministratori e valutatori gli strumenti per monitorare i risultati della ricerca, aumentarne la visibilità e allocare in modo efficace le risorse disponibili.
EnglishThe ternary system NieSneTe was investigated by means of light optical microscopy (LOM), powder Xray diffraction (XRD), differential thermal analysis (DTA) and scanning electron microscopy (SEM) in combination with energy dispersive X-ray spectroscopy (EDX). Two isothermal sections at 600 and 800 C were investigated experimentally. The two ternary compounds, Ni5.78SnTe2 (space group I4/mmm, Pearson symbol tI18) and Ni3xSnTe2 (space group P63/mmc, Pearson symbol hP12), already known from literature, were confirmed, although Ni3xSnTe2 was found only at 600 C. At higher temperatures a continuous phase field of the general NiAs-type structure was discovered between NiTe2x and Ni3Sn2 HT. It ranges continuously from 34 to 63 at.% Ni, covering CdI2-types, as well as Ni2In-type domains; thus a continuous transition from the CdI2 to Ni2In type is confirmed, to the best of our knowledge, for the first time. Lattice parameter variations and the transition CdI2eNiAseNi2In in the ternary phase field were analysed. Furthermore, vertical sections at 10, 40, 55, 60 and 70 at.% Ni were determined. A liquidus surface projection and a reaction scheme of the system were constructed as well. Altogether, 17 invariant phase reactions, including 3 eutectic reactions, 2 peritectic reactions, 11 transition reactions and one maximum were discovered.
Scheda prodotto non validato
Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo
| Titolo: | Phase equilibria and structural investigations of the general NiAs-type in the ternary system Ni-Sn-Te |
| Autori: | |
| Data di pubblicazione: | 2014 |
| Rivista: | |
| Abstract: | The ternary system NieSneTe was investigated by means of light optical microscopy (LOM), powder Xray diffraction (XRD), differential thermal analysis (DTA) and scanning electron microscopy (SEM) in combination with energy dispersive X-ray spectroscopy (EDX). Two isothermal sections at 600 and 800 C were investigated experimentally. The two ternary compounds, Ni5.78SnTe2 (space group I4/mmm, Pearson symbol tI18) and Ni3xSnTe2 (space group P63/mmc, Pearson symbol hP12), already known from literature, were confirmed, although Ni3xSnTe2 was found only at 600 C. At higher temperatures a continuous phase field of the general NiAs-type structure was discovered between NiTe2x and Ni3Sn2 HT. It ranges continuously from 34 to 63 at.% Ni, covering CdI2-types, as well as Ni2In-type domains; thus a continuous transition from the CdI2 to Ni2In type is confirmed, to the best of our knowledge, for the first time. Lattice parameter variations and the transition CdI2eNiAseNi2In in the ternary phase field were analysed. Furthermore, vertical sections at 10, 40, 55, 60 and 70 at.% Ni were determined. A liquidus surface projection and a reaction scheme of the system were constructed as well. Altogether, 17 invariant phase reactions, including 3 eutectic reactions, 2 peritectic reactions, 11 transition reactions and one maximum were discovered. |