Iron-base alloys (Fe-Cr) are proposed hereafter as materials for interconnect of planar-type intermediate temperature solid oxide fuel cell (ITSOFC); they are an alternative solution instead of the use of ceramic interconnects. These steels form an oxide layer (chrornia) which protects the interconnect from the exterior environment, but is an electrical insulator. One solution envisaged in this work is the deposition of a reactive element oxide coating, that slows down the formation of the oxide layer and that increases its electric conductivity. The oxide layer, formed at high temperature on the uncoated alloys, is mainly composed of chromia; it grows in accordance with the parabolic rate law (k(p) = 1.4 x 10(-12) g(2) cm(-4) s(-1)). On the reactive element oxide-coated alloy, the parabolic rate constant, k(p), decreases to 1.3 x 10(-13) g(2) cm(-4) s(-1). At 800 degrees C, the area-specific resistance of Fe-30Cr alloys is about 0.03 Omega cm(2) after 24 h in laboratory air under atmospheric pressure. The Y2O3 coating reduces the electrical resistance 10-fold. This indicates that the application of Y2O3 coatings on Fe-30Cr alloy allows to use it as an interconnect for SOFC. (c) 2005 Elsevier B.V. All rights reserved.

Iron-base alloys (Fe-Cr) are proposed hereafter as materials for interconnect of planar-type intermediate temperature solid oxide fuel cell (ITSOFC); they are an alternative solution instead of the use of ceramic interconnects. These steels form an oxide layer (chromia) which protects the interconnect from the exterior environment, but is an electrical insulator. One solution envisaged in this work is the deposition of a reactive element oxide coating, that slows down the formation of the oxide layer and that increases its electric conductivity. The oxide layer, formed at high temperature on the uncoated alloys, is mainly composed of chromia; it grows in accordance with the parabolic rate law (kp= 1.4 × 10-12g2cm-4s-1). On the reactive element oxide-coated alloy, the parabolic rate constant, kp, decreases to 1.3 × 10-13g2cm-4s-1. At 800 °C, the area-specific resistance of Fe-30Cr alloys is about 0.03 Ω cm2after 24 h in laboratory air under atmospheric pressure. The Y2O3coating reduces the electrical resistance 10-fold. This indicates that the application of Y2O3coatings on Fe-30Cr alloy allows to use it as an interconnect for SOFC. © 2005 Elsevier B.V. All rights reserved.

Opportunity of metallic interconnects for ITSOFC: Reactivity and electrical property

Piccardo, P.
2006-01-01

Abstract

Iron-base alloys (Fe-Cr) are proposed hereafter as materials for interconnect of planar-type intermediate temperature solid oxide fuel cell (ITSOFC); they are an alternative solution instead of the use of ceramic interconnects. These steels form an oxide layer (chromia) which protects the interconnect from the exterior environment, but is an electrical insulator. One solution envisaged in this work is the deposition of a reactive element oxide coating, that slows down the formation of the oxide layer and that increases its electric conductivity. The oxide layer, formed at high temperature on the uncoated alloys, is mainly composed of chromia; it grows in accordance with the parabolic rate law (kp= 1.4 × 10-12g2cm-4s-1). On the reactive element oxide-coated alloy, the parabolic rate constant, kp, decreases to 1.3 × 10-13g2cm-4s-1. At 800 °C, the area-specific resistance of Fe-30Cr alloys is about 0.03 Ω cm2after 24 h in laboratory air under atmospheric pressure. The Y2O3coating reduces the electrical resistance 10-fold. This indicates that the application of Y2O3coatings on Fe-30Cr alloy allows to use it as an interconnect for SOFC. © 2005 Elsevier B.V. All rights reserved.
2006
Iron-base alloys (Fe-Cr) are proposed hereafter as materials for interconnect of planar-type intermediate temperature solid oxide fuel cell (ITSOFC); they are an alternative solution instead of the use of ceramic interconnects. These steels form an oxide layer (chrornia) which protects the interconnect from the exterior environment, but is an electrical insulator. One solution envisaged in this work is the deposition of a reactive element oxide coating, that slows down the formation of the oxide layer and that increases its electric conductivity. The oxide layer, formed at high temperature on the uncoated alloys, is mainly composed of chromia; it grows in accordance with the parabolic rate law (k(p) = 1.4 x 10(-12) g(2) cm(-4) s(-1)). On the reactive element oxide-coated alloy, the parabolic rate constant, k(p), decreases to 1.3 x 10(-13) g(2) cm(-4) s(-1). At 800 degrees C, the area-specific resistance of Fe-30Cr alloys is about 0.03 Omega cm(2) after 24 h in laboratory air under atmospheric pressure. The Y2O3 coating reduces the electrical resistance 10-fold. This indicates that the application of Y2O3 coatings on Fe-30Cr alloy allows to use it as an interconnect for SOFC. (c) 2005 Elsevier B.V. All rights reserved.
File in questo prodotto:
File Dimensione Formato  
2005-cabouro et al.pdf

accesso chiuso

Tipologia: Documento in versione editoriale
Dimensione 426.39 kB
Formato Adobe PDF
426.39 kB Adobe PDF   Visualizza/Apri   Richiedi una copia

I documenti in IRIS sono protetti da copyright e tutti i diritti sono riservati, salvo diversa indicazione.

Utilizza questo identificativo per citare o creare un link a questo documento: https://hdl.handle.net/11567/895332
Citazioni
  • ???jsp.display-item.citation.pmc??? ND
  • Scopus 71
  • ???jsp.display-item.citation.isi??? 64
social impact