IRIS è la soluzione IT che facilita la raccolta e la gestione dei dati relativi alle attività e ai prodotti della ricerca. Fornisce a ricercatori, amministratori e valutatori gli strumenti per monitorare i risultati della ricerca, aumentarne la visibilità e allocare in modo efficace le risorse disponibili.
EnglishIron-base alloys (Fe-Cr) are proposed hereafter as materials for interconnect of planar-type intermediate temperature solid oxide fuel cell (ITSOFC); they are an alternative solution instead of the use of ceramic interconnects. These steels form an oxide layer (chrornia) which protects the interconnect from the exterior environment, but is an electrical insulator. One solution envisaged in this work is the deposition of a reactive element oxide coating, that slows down the formation of the oxide layer and that increases its electric conductivity. The oxide layer, formed at high temperature on the uncoated alloys, is mainly composed of chromia; it grows in accordance with the parabolic rate law (k(p) = 1.4 x 10(-12) g(2) cm(-4) s(-1)). On the reactive element oxide-coated alloy, the parabolic rate constant, k(p), decreases to 1.3 x 10(-13) g(2) cm(-4) s(-1). At 800 degrees C, the area-specific resistance of Fe-30Cr alloys is about 0.03 Omega cm(2) after 24 h in laboratory air under atmospheric pressure. The Y2O3 coating reduces the electrical resistance 10-fold. This indicates that the application of Y2O3 coatings on Fe-30Cr alloy allows to use it as an interconnect for SOFC. (c) 2005 Elsevier B.V. All rights reserved.
Scheda prodotto non validato
Attenzione! I dati visualizzati non sono stati sottoposti a validazione da parte dell'ateneo
| Titolo: | Opportunity of metallic interconnects for ITSOFC: Reactivity and electrical property | |
| Autori: | ||
| Data di pubblicazione: | 2006 | |
| Rivista: | ||
| Abstract: | Iron-base alloys (Fe-Cr) are proposed hereafter as materials for interconnect of planar-type intermediate temperature solid oxide fuel cell (ITSOFC); they are an alternative solution instead of the use of ceramic interconnects. These steels form an oxide layer (chrornia) which protects the interconnect from the exterior environment, but is an electrical insulator. One solution envisaged in this work is the deposition of a reactive element oxide coating, that slows down the formation of the oxide layer and that increases its electric conductivity. The oxide layer, formed at high temperature on the uncoated alloys, is mainly composed of chromia; it grows in accordance with the parabolic rate law (k(p) = 1.4 x 10(-12) g(2) cm(-4) s(-1)). On the reactive element oxide-coated alloy, the parabolic rate constant, k(p), decreases to 1.3 x 10(-13) g(2) cm(-4) s(-1). At 800 degrees C, the area-specific resistance of Fe-30Cr alloys is about 0.03 Omega cm(2) after 24 h in laboratory air under atmospheric pressure. The Y2O3 coating reduces the electrical resistance 10-fold. This indicates that the application of Y2O3 coatings on Fe-30Cr alloy allows to use it as an interconnect for SOFC. (c) 2005 Elsevier B.V. All rights reserved. | |